KMID : 0381919950250040124
|
|
Korean Journal of Microscopy 1995 Volume.25 No. 4 p.124 ~ p.131
|
|
High Resolution TEM Observations in $Hg_{1-x}\;Tl_{x}\;Ba_{2}(Ca_{0.86}\;Sr_{0.14})_{2}\;Cu_{3}\;O_{8+\delta}$ Superconductors
|
|
Lee Hwack-Joo
Ryu Hyun
Park Yong-Ki
|
|
Abstract
|
|
|
High resolution transmission electron microscopic observations on the $Hg_{1-x}\;Tl_{x}\;Ba_{2}(Ca_{0.86}\;Sr_{0.14})_{2}\;Cu_{3}\;O_{8+\delta}$(x=0.00, 0.25, 0.50, 0.75) were carried out using side-entry type TEM working at 300 kV. The TEM samples are prepared by powder method. The pellets are crushed in agatar motar and suspended in $CCl_4$, solution and scooped in holely carbon microgrid. The 1223 structures are observed in all samples with [010] zone axis. Except x=0.25 sample, the lattice parameter a and c tend to decrease as the thallium contents are increased ranging from 0.3936 nm to 0.3713 nm for a, and from 1.6131 nm to 1.5138 nm for c parameter. Those of x=0.25 sample are reduced too much, 0.3785 nm for a, 1.5375 nm for c. The sample with x=0.25 shows the intergrowth of 1223 and 1234 structure with the ratio of 19 to 1. As the thallium content increases, the structures become more stable without having any defect. The samples are damaged by electron beam irradiation during the observation, however the structure can endure longer as the thallium contents are increased.
|
|
KEYWORD
|
|
High Resolution TEM, Superconductivity, Hg, T1-1223, Irradiation damage
|
|
FullTexts / Linksout information
|
|
|
|
Listed journal information
|
|
|
|