A Novel Mucoadhesive Polymer Film Composed of Carbopol, Poloxamer and Hydroxypropylmethylcellulose
|
|
Kim Tae-Hee
Ahn Jae-Soon Choi Hu Kyun Choi Yun-Jaie Cho Chong-Su
|
|
Abstract
|
|
|
Using the casting method novel mucoadhesive polymer blend film consisting of Carbopol, poloxamer, and hydroxypropylmethylcellulose (HPMC) was prepared and characterized. Triamcinolone acetonide (TAA) was loaded into Carbopol/poloxamer/HPMC polymer blend film. Carbonyl band of Carbopol in Carbopol/poloxamer/HPMC shifted to longer wavenumber than that of Carbopol in Carbopol/poloxamer due to the hydrogen bonding among Carbopol, poloxamer, and HPMC. Tan ¥ä peak assigned to glass transition temperature (Tg) of HPMC shifted to low temperature due to increased flexibility caused by increased poloxamer content in polymer blend films. Swelling ratio of Carbopol/poloxamer/HPMC films was lowest in Carbopol/ poloxamer/HPMC at mixing ratio of 35/30/35 (wt/wt/wt). Adhesive force of Carbopol/poloxamer/ HPMC films increased with increasing HPMC content in Carbopol/poloxamer/HPMC polymer blend film and increasing hydroxypropyl group content in HPMC due to hydrophobic property of HPMC although bioadhesive force was highest at mixing ratio of 35/30/35 (wt/wt/ wt). Release of TAA from TAA-loaded Carbopol/poloxamer/HPMC polymer blend film in vitro increased with increasing loading content of drug.
|
|
KEYWORD
|
|
Mucoadhesive, Polymer blend film, Carbopol, Poloxamer, Hydroxypropylmethyl cellulose, Transmucosal drug delivery
|
|
FullTexts / Linksout information
|
|
|
|
Listed journal information
|
|
|