KMID : 0358920010280010118
|
|
Journal of the Korean Academy of Pedodontics
2001 Volume.28 No. 1 p.118 ~ p.128
|
|
|
A STUDY ON TOOTHBRUSH ABRASION OF CERVICAL RESTORATIVE MATERIALS
|
|
Baik Byeong-Ju
Yang Jeong-Sook
Lee Doo-Cheol
Kim Jae-Gon
|
|
|
Abstract
|
|
|
|
This study was performed to evaluate the toothbrush abrasion characteristics of seven commercially available light-cured cervical restorative materials one resin-modified glass-ionomer material(Fuji II LC) three polyacid-modified composites(Compoglass, Dyract, F2000), and three light-cured composites(Heliomolar, Palpique Estelite, UniFil F). All samples were stored in distilled water at for 10 days. 2.0N of weight was loaded during the test and the abraded surfaces were examined with profilometer and SEM after 100,000 cycles. The results obtained were summarized as follows; 1. The highest hardness value of 79.7 was observed in the FT group and the lowest value of 20.0 was observed in the HM group. Results of Tukey test showed that an overall significant difference was indicated except the CG and DR groups(p<0.05). 2. The highest surface roughness was observed in the FL group and the lowest was observed in the UF group. Results of Tukey test showed the significant difference between the FL or FT and UF groups(p<0.05). 3. Statistically higher abrasion and surface roughness were observed for the dentifrice of paste type, Perio A+, than for that of gel paste type, Tom & Jerry. 4. The surface roughness values increased on the abraded surfaces because of the protrusion of filler particles due to selective removal of matrix resin.
|
|
|
KEYWORD
|
|
|
Abrasion characteristics, Toothbrush, Surface roughness, Hardness value
|
|
|
FullTexts / Linksout information
|
|
|
|
|
Listed journal information
|
|
|