Effects of heat treatment on the load-deflection properties of nickel-titanium wire
|
|
Chang Soo-Ho
Kim Kwang-Won
Lim Sung-Hoon
|
|
|
Abstract
|
|
|
|
Nickel-titanium alloy wire possesses excellent spring-back properties, shape memory and super-elasticity. In order to adapt this wire to clinical use, it is necessary to bend as well as to control its super-elastic force. The purpose of this study is to evaluate the effects of heat treatment on the load-deflection properties and transitional temperature range (TTR) of nickel-titanium wires. Methods: Nickel-titanium wires of different diameters ($0.016"\;{\times}\;0.022"$, $0.018"\;{\times}\;0.025"$ and $0.0215"\;{\times}\;0.028"$) were used. The samples were divided into 4 groups as follows: group 4, posterior segment of archwire (24 mm) without heat treatment; group 2, posterior segment of archwire (24 mm) with heat treatment only; group 3, anterior segment with bending and heat treatment; group 4, anterior segment with bending and 1 sec over heat treatment. Three point bending test was used to evaluate the change in load-deflection curve and obtained DSC (different scanning calorimetry) to check changes in $A_f$ temperature. Results: In the three point bending test, nickel-titanium wires with heat treatment only had higher load-deflection curve and loading and unloading plateau than nickel-titanium wires without heat treatment. Nickel-titanium wires with heat treatment had lower Af temperature than nickel-titanium wires without heat treatment. Nickel-titanium wires with heat treatment and bending had higher load-deflection curve than nickel- titanium wires with heat treatment and nickel-titanium wires without heat treatment. Nickel-titanium with heat treatment of over 1 sec and bending had the highest load-deflection curve. Nickel-titanium wires with heat treatment and bending had lower Af temperature, Nickel-titanium wires with heat treatment of over Af sec and bending had the lowest Af temperature. Conclusion: From the results of this study, it can be stated that heat treatment for bending of Nickel-titanium wires does not deprive the superelastic property but can cause increased force magnitude due to a higher load-deflection curve.
|
|
|
KEYWORD
|
|
|
Load-deflection curve, Three point bending, Nickel-titanium, Heat treatment
|
|
|
FullTexts / Linksout information
|
|
 
|
|
|
Listed journal information
|
|
  
|
|