Comparison Study of Wear Resistance Among Several Denture Teeth Opposing Various Restorative Materials
|
|
Park Young-Bae
|
|
|
Abstract
|
|
|
|
Partial or complete prosthesis is needed when teeth are lost due to various kinds of reason. Artificial teeth recover occlusion instead of natural teeth. Artificial teeth are required of esthetics, fragile resistance and abrasive resistance. Artificial tooth is made of acrylic resin or porcelain. Nowadays, acrylic resin artificial teeth are mainly used. Acrylic resin teeth are occluded with natural teeth, gold alloy, Ni-Cr alloy or porcelain etc. Acrylic resin teeth have similar translucency, gloss of natural teeth. And it has good chemical bond with denture base material, but it has low wear resistance. The aim of this study is to compare wear resistance among several denture teeth(Endura, SR-orthosit-PE, Planustar) and between artificial resin denture teeth and opposing 3 restorative materials(gold, Ni-Cr alloy, porcelain). Wear tests were conducted with a rotating wear testing apparatus(pin-on-disk type wear tester) under conditions of rpm 180, 75 minutes and constant loading of 50N. The upper part was the cusp of maxillary first molar and the lower part was a disk type restorative materials. To make similar oral environment, water was supplied continually. The acrylic resin teeth wear was determined by weighing the cusp each 5 minutes during 75 minutes test. Vicker’s hardness tester was used to evaluate the surface hardness of test specimens. The SEM was used to evaluate the wear surfaces. The results were as follows: 1. Wear rates of acrylic resin teeth opposing to the restorative materials were high in order of Porcelain, Gold, Ni-Cr alloy (p<.05). 2. Wear resistance rate opposing to the Porcelain disk, was shown in order of Endura, SR-orthosit-PE, Planustar. The wear rate of opposing to porcelain disk was above two times more than that of other groups (p<.05). 3. Wear resistance rates opposing to the Gold, Ni-Cr alloy disk, was shown in order of Endura, SR-orthosit-PE, Planustar (p<.05). 4. A degree of the surface hardness is directly proportional to the degree of wear resistance. There are statistically significant differences between each groups (p<.05).
|
|
|
KEYWORD
|
|
|
Artificial resin denture teeth, Porcelain, Gold alloy
|
|
|
FullTexts / Linksout information
|
|
|
|
|
|
Listed journal information
|
|
|
|