Composition of nickel-chromium alloy on the centrifugal casting and the influence of quantitative of oxides on the casting temperature
|
|
Kim Won-Soo
|
|
Abstract
|
|
|
Purpose: The aim of this study was to analysis the composition on the centrifugal casting and the oxide on the casting temperature.
Methods: The nickel based alloy were used in this study. Wax pattern specimens (10*10*2) were invested with phosphate-bonded investment in metal rings, the liquid/powder ratio and overall burn-out schedules for these investments were followed in accordance with the manufacturer¡¯s instructions. After casting, the alloy specimens were evaluated as regards composition(EPMA). The casting temperatures were as follows: 1400¡É and 1700¡É. The quantitative analysis of oxides were scanning electron microscope(SEM), energy dispersive spectroscopy(EDS) and line scanning.
Results: Nearer the injection lines showed that there is a large amount of nickel. Quantitative of oxides of Ni-Cr alloy cast from 1400¡É is lager than Ni-Cr alloy cast from 1700¡É
Conclusion: Casting when using a centrifugal casting machine centrifugal force affects the composition of the alloy. The higher the temperature, the amount of oxide that is generated many.
|
|
KEYWORD
|
|
Beryllium, Casting, Dental alloy, Ni-Cr alloy
|
|