Journal of The Korean Research Society for Dental Materials 2007 Volume.34 No. 2 p.29 ~ p.36
|
|
Micro-Nano Structure Formation on Ti-Ag Alloy for Dental Implants
|
|
Moon Seung-Kyun
Kang Dong-Kuk Joo Uk-Hyon Oh Keun-Taek Hwang Jae-Sun Kim Kwang-Man Kim Kyoung-Nam
|
|
Abstract
|
|
|
Surface topography is crucial for the short and long term success of dental implants. It is known that surface roughness in the range of 1-10 § maximizes the interlocking between the bone and the surface of the implant. On the other hand, it is reported that osseointegration is promoted on surfaces of nano-metric level because surface profiles in the nano-metric level play an important role in the adsorption of proteins. Therefore hybrid surface consisted of micro and nanopore is expected to be the new surface treatment on Ti-Ag alloy for dental implants. The titanium-silver alloy developed for biomedical applications had better mechanical properties and corrosion resistance than pure titanium. And there has been no research on surface modification of titanium-silver alloy for dental implants. Therefore, the present paper reported on the formation of hybrid surface on titanium-silver alloy. The specimens were grit-blasted to obtain micro pore on the surface. After grit-blasting, the specimens were anodized at different anodizing voltages (20, 50 and 80V) for different times (10, 20, 40 and 60 min), in 0.5% HF aqueous solution at room temperature using a DC power supply. The surface topography of titanium-silver alloy was characterized by field emission scanning electron microscope (FE-SEM). It was believed that the topography of the hybrid surface was affected by electrochemical conditions. When titanium-silver alloy was anodized at 20 V for 1 hour, hybrid surface was uniformly formed. Therefore, it was considered that this surface treatment would be adapted cautiously to titanium-silver alloy for dental implants.
|
|
KEYWORD
|
|
anodic oxidation, grit-lasting, hybrid surface, micropore, nanopore, titanium-silver alloy
|
|
FullTexts / Linksout information
|
|
|
|
Listed journal information
|
|
|
|