The material of choice for functional and esthetic reconstruction of maxillofacial defects is silicone. Silicone has appropriate physical properties for maxillofacial prosthesis but it has weak edge strength. Therefore, a proper combination of silicone and polyurethane sheet is recommended to improve this weakness. Various primers are also used to enhance the adhesive strength between silicone and polyurethane sheet. The purpose of this study was to determine the adhesive strength of silicone and polyurethane sheet. Silicone elastomer mixture was made by admixing MDX4-4210 elastomer (40％) and silastic Medical Adhesive Type A(60％). This silicone elastomer mixture was attached to polyurethane sheet, using one of three different primers(1205, S-2260, or A-304), treated for 1, 2, 4, 6, and 8 hours. These were then polymerized in room temperature, dry-heat oven or microwave oven. Six specimens per each groups, a total of 270 specimens were prepared for final test. The differences of T-peel bonding strengths were then determined by a test. The differences of T-peel bonding strengths were then determined by a test method that was recommended by American Society for Testing and Materials C794-80. The results were statistically analyzed using the ANOVA and Mutiple Range Tests(Tukey´ HSD). The reults were as follow. 1. Type of primer, primer reaction time, and methods of polymerization showed significant correlation on the T-peel bonding strengths in adhesiveness between silicone and polyurethane sheet.
2. A-304 primer showed statistically higher in T-peel bonding strength than otehr type of primers except for the polymerization in microwave oven with reaction times of 2, 6 hours(p＜0.05). 3. No significant differences in T-peel bonding strength were observed among the polymerization methods. 4. The effect of reaction time by the primer type and polymerization method showed statistically significant differences in bonding strength among different reaction times. And in most cases, reaction time of 1 or 2 hours showed higher T-peel bonding strength.
|