Poly (L- lactic acid-co-glycine-L-lactic acid) and Poly (L-lactic acid-co-glycine-L- methyl lactic acid ) have been prepared by ring opening polymerization. The monomer 6, 6-dimethyl morpho-line-2, 5-dione was synthesized by the bromoisobutylation of 2-bromoisobutyryl bromide with glycin e. L-lactide, 6-methyl morpholine-2, 5-diode. and 6, 6-dimethyl morpholine-2, 5-diode have been used as starting materials for polydepsipeptides. The synthesized monomers and copolymers have been identified by NMR and FT-lR spa- ctrophotometer. The thermal propert ies and glass transition temperature(Tg) of the copolymers have been measured by differential scanning calorimetry. The Tg values of poly(L-lactic acid co-glycine-L-lactic acid) system are increased from 53°C to 107°C with increasing the mole fraction of 6-methyl morpholine-2, 5-diode. And the Tg values of poly(L-lactic acid co-glycine-L-methyl lactic acid) system are increased from 53°C to 138°C with increasing the mole fraction of 6. 6-dimethyl morpholine-2, 5-diode The thermal stability of poly (L-lactic acid-co-glycine-L-methyl lactic acid) is slightly greta text than that of poly(L-lactic acid-co-glycine-L-lactic acid) due to the methyl group.
|