HRTEM Observations on ZnSe/GaAs Interfaces Grown by MBE
|
|
Lee Hwack-Joo
Ryu Hyun
Park Hae-Sung
Kim Tae-Il
|
|
|
Abstract
|
|
|
|
The interfacial structures of ZnSe/GaAs which were grown by single chamber MBE at $300^{\circ}C$ were investigated by high resolution transmission electron microscope working at 300 kV with resolution of 0.18 nm. The interfaces of ZnSe/GaAs whose thickness is 2,700 nm are wavy and extensive stacking faults were formed in ZnSe epilayer but the interfaces maintained the coherency with the substrate GaAs. The stacking faults are formed in {111} planes and their sizes are $10{\sim}20nm$ in length and two or three atomic layer in width with the density of $10^9/cm^2$. Micortwins and moire fringes are also observed. However. in 10 nm ZnSe epilayer, the interfaces are pseudomorphic and only moire fringes are observed in local areas. The cylindrical defects which are perpendicular to the interface with $50{\sim}60nm$ in length, were observed with the interval of 50 nm at ZnSe/GaAs interfaces in 2,700nm epilayer. The origin and character of these defects are unknown, however, they played a role of producing the structural defects at the interfaces.
|
|
|
KEYWORD
|
|
|
|
|
|
FullTexts / Linksout information
|
|
|
|
|
Listed journal information
|
|
|