This study was carried out to investigate characteristic of vinyl chloride emissioned from poly vinyl chloride extrusion process and to evaluate the efficiency of local exhaust ventilation system. Before local ventilation facility was constructed in poly vinyl chloride extrusion process, the average worker exposure to vinyl chloride was 3.15 ppm, which exceeded Threshold Limit Value of American Conference of Governmental Industrial Hygienists(ACGIH-TLV), 1 ppm, It is possible that vinyl chloride residues in the poly vinyl chloride resin was released or degased due to extrusion heat. The larger the width of vinyl tube become, the higher worker exposure to vinyl chloride was. It is estimated that vinyl chloride from vinyl chloride resin increased as amount of poly vinyl chloride resin extruded in the extrusion process increased. Canopy hood was an appropriate type for poly vinyl chloride resin extrusion process. This local exhaust ventilation has fan static pressure of 7.65 inch wg (190 ㎜H₂O), total volumetric flowlate of 4,796 CFM (135.8 ㎥/min) and fan power requirement of 12 hp (8.952 Kw). After this local exhaust ventilation was constructed there, the average concentration of worker exposure to vinyl chloride was reduced to be 0.46 ppm, which was below the Threshold Limit Value, 1 ppm. Also, the removal efficiency rate of vinyl chloride attained by local exhaust ventilation was 85.3%. It was a statistically significant (p$lt;0.01).
|