KMID : 1004520170330020080
|
|
Journal of Dental Rehabilitation and Applied Science
2017 Volume.33 No. 2 p.80 ~ p.87
|
|
|
Physical properties of a new resin-based root canal sealer in comparison with AH Plus Jet
|
|
Myint Thu
Kim Jin-Woo
Park Se-Hee
Cho Kyung-Mo
|
|
|
Abstract
|
|
|
Purpose: The aim of this study was to assess the physical properties of a novel resin-based endodontic sealer, Any-Seal, in comparison with AH Plus Jet.
Materials and Methods: Flow, radiopacity and compressive strength were examined according to ISO 6876/2001. For flow test, 0.05 mL of sealer was placed between glass plate and 100 g weight were applied. Ten minutes after mixing the sealers, the load was removed and the diameters of the compressed sealer discs were measured. For radiopacity, 10 mm diameter and 1 mm thickness sample were fabricated and took radiograph with an aluminum step-wedge and analyzed using imaging program. For compressive strength test, 4 mm × 6 mm cylindrical specimen was fabricated and tested after 24 hours and 1 week using Universal testing machine.
Results: Both tested sealers were consistent with ISO 6876/2001 in the flow and radiopacity test. The flow values of both sealers were not significantly different (P > 0.05). AH Plus Jet had significantly higher radiopacity (P < 0.05). AH Plus Jet showed higher compressive strength at both time intervals (P < 0.05).
Conclusion: Any-Seal showed low compressive strength until after 1 week, so its physical and biological aspect should be evaluated more before clinical use.
|
|
|
KEYWORD
|
|
|
AH Plus Jet, Any-Seal, compressive strength, flow, radiopacity
|
|
|
FullTexts / Linksout information
|
|
|
|
|
Listed journal information
|
|
|