Journal of Korean Ophthalmic Optics Society 2011 Volume.16 No. 1 p.13 ~ p.19
|
|
Studies on the Cellulose Acetate Glasses Frame Sheet
|
|
Lee Hae-Sung
Lee Sung-Jun Jung Sang-Won Kim Hyun-Chul Kim Eun-Joo Go Young-Jun Lee Se-Guen
|
|
Abstract
|
|
|
Purpose: The purpose of this study was to assess characterize overseas company¡¯s Cellulose acetate glasses frame sheets (overseas company¡¯s CA sheet) Also, the optimum content of plasticizer and melt extrusion condition of industrial CA resin were established for appropriate glasses frame.
Methods: Overseas company¡¯s Cellulose acetate glasses frame sheets (overseas company¡¯s CA sheet) were characterized by 1H-NMR, GPC, and TGA. Also, the optimum content of plasticizer and melt extrusion condition of industrial CA resin were established.
Results: The plasticizer of overseas company¡¯s CA sheet measured by 1H-NMR was diethyl phthalate, and its content was measured 30 wt% by TGA. Also, industrial CA resin showed enough melting behavior in the range of 190~200oC. Compared to overseas company¡¯s CA sheet¡¯s tensile strength value of 2.2~2.8 kgf/mm2, industrial CA resin exhibited sufficient tensile strength value of 2.3 kgf/mm2 for glasses frame.
Conclusions: Industrial CA resin with 30 wt% plasticizer content would be a promising material for glasses frame prepared by melt extrusion to replace China CA sheet.
|
|
KEYWORD
|
|
Cellulose acetate, Glasses frame, Melt processing
|
|