Effect of non-thermal atmospheric pressure nitrogen andair plasma on the surface properties and the disinfection of denture base resin
|
|
Seo Hye-Yeon
Yoo Eun-Mi Choi Yu-Ri Kim Soo-Hwa Kim Kwang-Man Kim Kyoung-Nam
|
|
Abstract
|
|
|
Objectives : The purpose of this study was to investigate the effect of non-thermal atmospheric pressure plasma jet(NTAPPJ) on surface properties and Streptococcus mutans disinfection of denture base resin.
Methods : Self-cured denture base resin (Jet denture repair resin, Lang dental Mfg, co., USA) was used to make specimen(12 mm ¡¿ 2 mm). To observe surface change before and after plasma process, surface roughness and contact angle were measured. For sterilization experiments, the surfaces of specimens were treated with nitrogen and air NTAPPJ for 1 minute after S. mutans was inoculated on the material surfaces.
Results : Before plasma process, surface roughness of denture base resin was 0.21 ¡×¡©¡¾ 0.02 ¡×¡©. After air and nitrogen NTAPPJ process, surface roughness was 0.19 ¡×¡©¡¾ 0.03 ¡×¡©and 0.18 ¡×¡©¡¾ 0.01 ¡×¡©respectively. There was no significant difference(p>0.05). Contact angle of control group without plasma process was 83.81©¬¡¾ 3.14©¬, while after plasma treatment, contact angles of air NTAPPJ and nitrogen NTAPPJ groups were 63.29©¬¡¾ 2.27©¬and 46.68©¬¡¾ 5.82©¬respectively. The result showed a significant decrease in contact angle after plasma process(p<0.05). Compared to the control group 6020.33(CFU/mL) without plasma process, CFU decreased significantly after air NTAPPJ 90.75(CFU/mL) and nitrogen NTAPPJ 80.25(CFU/mL) treatment(p<0.05).
Conclusions : It was considered that NTAPPJ can be used for denture disinfection without changing surface properties of materials.
|
|
KEYWORD
|
|
denture base resin, disinfection, non-thermal atmospheric pressure plasma
|
|