Influence of Low Temperature Degradation on Bond Strength of Yttria-Stabilized Tetragonal Zirconia Polycrystal Core to Veneering Ceramic
|
|
Kim Ki-Baek
Kim Jae-Hong
|
|
Abstract
|
|
|
The purpose of this study was to evaluate the influence of low temperature degradation (LTD) on the bonding strength of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP). The push-shear bond test method was used to investigate the core-veneer bonding strength of industrially manufactured Y-TZP core ceramic and manufacturer recommended veneering ceramic. Four groups from ceramic-zirconia specimens (n=28; n=7 per group) were assigned into four experimental aging conditions, namely storage in an autoclave at 134¡É for 0, 3, 5, 10 hours. Bonding strength was obtained using a universal testing machine with crosshead speed 0.5 mm/min. Data were statistically analyzed using one-way ANOVA and Tukey.s test (¥á=0.05). In bonding strength test, the group which was treated with LTD showed lower bonding strength than no treated group. The ceramic-zirconia bonding strength was affected by LTD (p<0.05). Digital microscope examination of the fracture surface showed mixed failures with adhesive and cohesive types in LTD with treated Y-TZP groups.
|
|
KEYWORD
|
|
Autoclave , Bonding strength , Low temperature degradation , Yttria-stabilized tetragonal zirconia polycrystal
|
|
FullTexts / Linksout information
|
|
|
|
Listed journal information
|
|
|