KMID : 1034420160410030189
|
|
Restorative Dentistry & Endodontics 2016 Volume.41 No. 3 p.189 ~ p.195
|
|
In vitro evaluation of a newly produced resin-based endodontic sealer
|
|
Song Yoo-Seok
Choi Yoorina Lim Myung-Jin Yu Mi-Kyung Hong Chan-Ui Lee Kwang-Won Min Kyung-San
|
|
Abstract
|
|
|
Objectives: A variety of root canal sealers were recently launched to the market. This study evaluated physicochemical properties, biocompatibility, and sealing ability of a newly launched resin-based sealer (Dia-Proseal, Diadent) compared to the existing root canal sealers (AHplus, Dentsply DeTrey and ADseal, Metabiomed).
Materials and Methods: The physicochemical properties of the tested sealers including pH, solubility, dimensional change, and radiopacity were evaluated. Biocompatibility was measured using the 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. For microleakage test, single-rooted teeth were instrumented, and obturated with gutta-percha and one of the sealers (n = 10). After immersion in 1% methylene blue solution for 2 weeks, the specimens were split longitudinally. Then, the maximum length of staining was measured. Statistical analysis was performed by one-way analysis of variance followed by Tukey test (p = 0.05).
Results: Dia-Proseal showed the highest pH value among the tested sealers (p < 0.05). ADseal showed higher dimensional change compared to AHplus and Dia-Proseal (p < 0.05). The solubility values of AHplus and Dia-Proseal were similar, whereas ADseal had the lowest solubility value (p < 0.05). The flow values of sealer in increasing order were AHplus, DiaProseal, and ADseal (p < 0.05). The radiopacity of AHplus was higher than those of ADseal and Dia-Proseal (p < 0.05). The cell viability of the tested materials was statistically similar throughout the experimental period. There were no significant differences in microleakage values among the tested samples.
Conclusions: The present study indicates that Dia-Proseal has acceptable physicochemical properties, biocompatibility, and sealing ability.
|
|
KEYWORD
|
|
Biocompatibility, Microleakage, Physicochemical, Sealer
|
|