Restorative Dentistry & Endodontics 2017 Volume.42 No. 3 p.206 ~ p.215
|
|
Effects of air-abrasion pressure on the resin bond strength to zirconia: a combined cyclic loading and thermocycling aging study
|
|
Al Shehri Eman Z.
Al Zain Afnan O. Sabrah Alaa H. Al Angari Sarah S. Al Dehailan Laila Eckert George J. Platt Jeffrey A. Ozcan Mutlu Bottino Marco C.
|
|
Abstract
|
|
|
Objectives: To determine the combined effect of fatigue cyclic loading and thermocycling (CLTC) on the shear bond strength (SBS) of a resin cement to zirconia surfaces that were previously air-abraded with aluminum oxide (Al2O3) particles at different pressures.
Materials and Methods: Seventy-two cuboid zirconia specimens were prepared and randomly assigned to 3 groups according to the air-abrasion pressures (1, 2, and 2.8 bar), and each group was further divided into 2 groups depending on aging parameters (n = 12). Panavia F 2.0 was placed on pre-conditioned zirconia surfaces, and SBS testing was performed either after 24 hours or 10,000 fatigue cycles (cyclic loading) and 5,000 thermocycles. Non-contact profilometry was used to measure surface roughness. Failure modes were evaluated under optical and scanning electron microscopy. The data were analyzed using 2-way analysis of variance and ¥ö2 tests (¥á = 0.05).
Results: The 2.8 bar group showed significantly higher surface roughness compared to the 1 bar group (p < 0.05). The interaction between pressure and time/cycling was not significant on SBS, and pressure did not have a significant effect either. SBS was significantly higher (p = 0.006) for 24 hours storage compared to CLTC. The 2 bar-CLTC group presented significantly higher percentage of pre-test failure during fatigue compared to the other groups. Mixed-failure mode was more frequent than adhesive failure.
Conclusions: CLTC significantly decreased the SBS values regardless of the air-abrasion pressure used.
|
|
KEYWORD
|
|
Air-abrasion, Bond strength, Fatigue, Panavia F 2.0, Resin cement, Thermocycling
|
|