KMID : 1035320160430010081
|
|
Korean Society for Dental Materials
2016 Volume.43 No. 1 p.81 ~ p.89
|
|
|
Effect of Experimental Fluoride Varnish upon the Vickers Hardness of Bovine Teeth
|
|
Kim Ah-Jin
Son Ju-Lee
Oh Seung-Han
Bae Ji-Myung
|
|
|
Abstract
|
|
|
|
The purpose of this study was to evaluate the effect of the experimental and commercial fluoride varnishes on the Vickers hardness of bovine teeth. The experimental fluoride varnishes with 5 wt.% NaF were fabricated using Bis-GMA or rosin as the resin base. The components were mixed with over-head stirrer under warming up in a double boiler for 30 minutes. Four commercial fluoride varnishes (V-varnish, Flor-opal, Cavity shield, Fluor protector) were compared with the experimental fluoride varnishes. Vickers hardness was measured on the labial surface of bovine anterior teeth after applying fluoride varnish on 5th and 30th day. The surface of bovine teeth was observed with a scanning electron microscope before and after applying fluoride varnish and the change of the components on the bovine teeth surface was measured with EDX. In terms of hardness, the experimental rosin-based fluoride varnish showed significantly higher hardness on the 5th and 30th day than the control (bovine teeth without fluoride treatment)(p<0.05). EDX results showed that the fluoride content on the surface of bovine teeth treated with the experimental rosin-based fluoride varnish was highest on the 1st and 10th day. The higher hardness and fluoride content of experimental rosin-based fluoride varnish can be considered to be used as an effective fluoride varnish to prevent dental caries.
|
|
|
KEYWORD
|
|
|
Fluoride varnish, Vickers hardness, bis-GMA-based, Rosin-based
|
|
|
FullTexts / Linksout information
|
|
|
|
|
Listed journal information
|
|
|