Development of fluoride varnish with sustained fluoride release and biocompatibility
|
|
Shin Kyung-Su
Kim Ah-Jin
Oh Seung-Han
Bae Ji-Myung
|
|
|
Abstract
|
|
|
|
The purpose of this study was to fabricate a biocompatible fluoride varnish with sustained fluoride release, and to compare it with commercial fluoride varnishes. For the experimental fluoride varnish, bis-GMA (BG) or two types of rosin (KR-610: K0, KR-612: K2) were used as bases. Either ethyl acetate or ethanol was added as solvent and 5 wt% NaF was used. 5 mg of experimental F- varnishes and 2 commercial products, Cavity shield (CS) and Flor-opal (FO), were applied on a labial surface of bovine teeth (10 mm × 7 mm). The amount of fluoride release was measured at 1 hr, 2 hrs, 3 hrs, 4 hrs, 8 hrs, 12 hrs, 1 day, 3 days, 5 days, 10 days, 15 days, 20 days and 30 days. MTT test was done with diluted F- varnishes using ethanol. Statistical analysis was done with one-way ANOVA and Duncan multiple range test (α=0.05). BG showed the highest fluoride release at 1 hr (P<0.05), while that of K0 was highest at 2 hrs (P<0.05). From 1 day to 5 days, experimental fluoride varnishes showed higher fluoride release than the commercial products (P<0.05), and there were no significant differences after 5 days (P>0.05). For MTT test, K0 and FO showed higher cell viability than other experimental groups (P<0.05), with no significant differences with K2 (P>0.05). Considering the sustained fluoride release and cell viability of the experimental rosin-based fluoride varnishes compared with commercial products, it will be appropriate for clinical application.
|
|
|
KEYWORD
|
|
|
fluoride varnish, fluoride release, cell viability, rosin-based
|
|
|
FullTexts / Linksout information
|
|
|
|
|
Listed journal information
|
|
|
|