Characteristics of Antibacterial Chlorhexidine-Containing Hydroxyapatite Coated on Titanium
|
|
Kim Min-Hee
Hwang Moon-Jin
Lee Woon-Young
Park Young-Jun
Song Ho-June
|
|
|
Abstract
|
|
|
|
In this study, antibacterial chlorhexidine (CHX)-containing hydroxyapatite (HAp) was coated on titanium and investigated its characteristics. Ti-mSBF-CHX group was prepared by soaking titanium disks in the modified simulated body fluid (mSBF) mixed with CHX. Ti-mSBF group was coated using mSBF without CHX. Ti-mSBF-adCHX group was prepared by soaking Ti-mSBF specimen in CHX-containing solution. The crystallines clusters composed with nano-shaped crystallites were coated on the surface of the Ti-mSBF specimen. The ribbon-shaped crystallites were observed with the crystalline clusters on the Ti-mSBF-CHX specimen. The content of CHX chemical compositions was high in ribbon-shaped crystallites. HAp crystalline structure was dominant for all prepared specimens, and β-TCP (tricalcium phosphate) and OCP (octacalcium phosphate) crystalline structures were observed in the Ti-mSBF-CHX specimen. FT-IR spectra showed the strong peaks of CHX in Ti-mSBF-adCHX and Ti-mSBF-CHX groups. However, after immersing in a phosphate buffered saline (PBS), CHX was rapidly released in Ti-mSBF-adCHX group, while it was slowly released in Ti-mSBF-CHX. We expect that the coating method of Ti-mSBF-CHX group could be used for protecting inflammation of titanium implant by incorporating antibacterial agent CHX into HAp layer.
|
|
|
KEYWORD
|
|
|
Chlorhexidine, Coprecipitation, Hydroxyapatite, Simulated body fluid, Titanium
|
|
|
FullTexts / Linksout information
|
|
|
|
|
Listed journal information
|
|
|