1979 Volume.21 No. 2 p.11 ~ p.19
|
|
|
Studies on Sericin Fixation by Use of Alum Meal
|
|
Choe Byong-Hee
Nahm Joong-Hee
|
|
|
Abstract
|
|
|
|
This has been carried out how the sericin insoluble fixations of raw silk should be with potassium alum. This is learned from the leather tanning technique which the process works with collagen, a kind of proteins. Former reports had shown such works, however, they did not consider the moisture absorbability after their process reports by using chromium alum, formalin or vinyl acetate grafting. This report, however, paid attention to protect such absorbability as well as sericin fixation, so far it may be useful for plactical use of silk. In order to clear how the sericin is fixed with such chemicals, fundermental mechanism of weding process and chemical reaction against proteins were also discussed. The obtained results of the report are as followings. 1. Alum should not be treated for raw silk with high temperature bath like other reports because such treat induces raw silk to be stiffly after the treat. 2. It is recommended that raw silk should be treated with alum solution at room temperature for more than three hours. Even in this case, the use of only alum with raw silk could to fix sericin some how, but it increased the water proofness of the silk. 3. 1% of alum solution was found to be able to fix the sericin of raw silk. 4. In case we consider only sericin fixations, a combination treat of 1% alum for three hours and 0.5% NaOH for ten minutes method showed the best result. 5. In case we consider sericin insoluble fixation and moisture absorbility, the reversive combination of the above process was found to be the best results. 6. Sericin fixing evidence was shown with drying feature curves of wed each treated silk where we could to analyze how the chemical nature is changed after each treat. 7. Deguming ratio may be obtained up to 4.3% after the alum combination treat with regular raw silk. Such ratio was considered to be good enough for the purpose when the textile is washed with warm soap water. 8. Moisture absorbability of the combination treat of alum and NaOH was found to be good enough as well as non treated silk. 9. The tenacity and elongation of the treated silk did not change even after three month. 10. Above all, this method is considered to be better process than other coloured fixing (tannin method. Cr-alum method) or smell fixing (formalin method. vinyl acetate method).
|
|
|
KEYWORD
|
|
|
|
|
|
FullTexts / Linksout information
|
|
|
|
|
|
Listed journal information
|
|
|
|
|