An IRS Study on the Adsorption of Carbonmonoxide on Silica Supported Ni-Cu Alloys
|
|
Ahn Jeong-Soo
Yoon Koo-Sik Park Sang-Youn Park Sung-Kyun
|
|
Abstract
|
|
|
We have investigated the infrared spectra for CO adsorbed on silica supported nickel(Ni-SiO2),silica supported copper(Cu-SiO2), silica supported nickel-copper alloys(Ni/Cu-SiO2) of several compositions with varying CO pressures(0.2 torr¡50 torr) at room temperature and on pumping to vacumn at room temperature within the frequency range of 1500 cm-1 ¡2500 cm-1. Four bands(2059.6 cm-1, ¡2036.5 cm-1, ¡ 1868.7 cm-1, ¡1697.1 cm-1) were observed for Ni-SiO2, two bands(¡2115.5 cm-1, ¡1743.0 cm-1) were observed for Cu-SiO2 and five bands(¡2123.2 cm-1, 2059.6 cm-1,¡2036.4 cm-1, ¡1899.5 cm-1, ¡1697.1 cm-1) were observed for Ni/Cu-SiO2. These absorption bands correspond with those of the previous reports approximately. The bands below 1800 cm-1 were only observed with Ni metal or Ni/Cu alloy crystal plane containing step at room temperature and the ¡1697.1 cm-1 bands observed with Ni-SiO2 and Ni/Cu-SiO2 may
be ascribed to CO molecule adsorbed on the adsorption sites near step. The bands below 2000 cm-1 were rarely observed with Cu metal crystal plane at room temperature and the 1743.0 cm-1 bands may be ascribed to CO molecule adsorbed on the adsorption sites near step. The band shifts of adsorbed CO with varing Cu contents from 0 to 0.5 mole fraction at the same CO pressure or at the same pumping time to vacumn were below 21 cm-1. and comparatively small than those with other ¥°B metal addition. It may means ligand effect of Cu delectron is small.
|
|
KEYWORD
|
|
CO adsorption, Ni/Cu alloy, Silica supported Ni/Cu alloy, CO adsorption on silica supported Ni/Cu alloy
|
|