Mechanical properties and cytotoxicity of PLA/PCL films
|
|
Jeong Hee-Seok
Rho Jeong-Won Shin Ji-Yeon Lee Deuk-Yong Hwang Tae-Seon Kim Kwang-J.
|
|
Abstract
|
|
|
Thermodynamically immiscible poly(lactic acid) (PLA) and poly(¥å-caprolactone) (PCL) were blended and solution-cast by adding the 3% compatibilizer (tributyl citrate, TBC) of the PCL weight. In the PLA/PCL composition range of 99/1?95/5 wt%, mechanical properties of the PLA/PCL films with TBC were always superior to those of the films without TBC. The tensile strength of 42.9?¡¾?3.5 MPa and the elongation at break of 10.3?¡¾?2.7% were observed for the 93/7 PLA/PCL films without TBC, indicating that PCL addition is effective for strength and ductility. However, the tensile strength of 54.1?¡¾?3.4 MPa and the elongation at break of 8.8?¡¾?1.8% were found for the 95/5 PLA/PCL with TBC, indicating that the effect of co-addition of PCL and TBC on mechanical properties of the films is more pronounced. No cytotoxicity was observed for the PLA/PCL films regardless of TBC addition.
|
|
KEYWORD
|
|
Poly(lactic acid), Poly(¥å-caprolactone), Compatibilizer, Tensile strength, Cytotoxicity, Cell proliferation
|
|
FullTexts / Linksout information
|
|
|
|
Listed journal information
|
|
|