A Study of Characteristic and Preparation of TiO2, BaTiO3 Thin Film by Sol-gel Method
|
|
Kim Ha-Rim
Jeong Ju-Hyun
|
|
Abstract
|
|
|
Purpose : In this study, TiO2, BaTiO3 thin films were prepared from metal naphthenates by sol-gel and the properties of the films have been studied. High resolution X-ray diffraction, field emission scanning electron microscope and UV spectrophotometer were used to analyze film¡¯s property.
Methods : The precursor sol was spin-coated onto the soda-lime-silica glass at 1500 rpm for 10 sec. Prefired films were finally annealed at 500¡É for 30 min in air. The crystal structure and crystallinity of the films were investigated by High Resolution X-ray diffraction system. Surface character of the annealed film was evaluated by field emission scanning electron microscope and scanning probe microscope. The transmittances in the UV(200-380 nm), visible(380-750 nm) and NIR(750-900 nm) range was measured by UV visible NIR spectrophotometer.
Results : The TiO2 films was crystallized into anatase and BaTiO3 film has not been identified for its peak. The transmittances at visible wavelength range for TiO2, BaTiO3 film was 80% or more, BaTiO3 film had higher UV and blue light blocking than TiO2 film.
Conclusion : BaTiO3 film had a higher blocking rate of ultraviolet and blue light than TiO2 film, and the visible light transmission rate was measured at more than 80% from all Film.
|
|
KEYWORD
|
|
Blue light, Sol-gel, Spin coating, Transmittance
|
|