KMID : 0988720090250040437
|
|
Journal of the Korean Academy of Stomatognathic Function and occlusion 2009 Volume.25 No. 4 p.437 ~ p.444
|
|
|
|
Song Chang-Kyu
Park Se-Hee Kim Jin-Woo Cho Kyung-Mo
|
|
Abstract
|
|
|
The purpose of this study was to evaluate the physical properties of different automixing resin cements and the shear bond strength on dentin. For this study, two self-adhesive automixing resin cement(Rely-X Unicem(3M ESPE, St. Paul, USA), Embrace resin cement(Pulpdent, Oakland, USA)) and one chemical polymerizing resin cement(Resiment Ready-Mix(J.L.Blosser Inc., Liberty Missouri, USA)) were used. To evaluate the physical properties, compressive strength, diametral tensile strength and flexural strength were measured. The specimens were fabricated using Teflon mould according to manufacturers¡¯ instructions and stored for 24 hours in an atmosphere of 100% humidity. To evaluate the shear bond strength on dentin, each cements were adhered to buccal dentinal surface of extracted human lower molars in 2mm diameter. Physical properties and shear bond strengths were measured using universal testing machine(Z010, Zwick GmbH, Ulm, Germany) at a crosshead speed of 0.5mm/min. The physical properties and shear bond strength of different automixing resin cements were statistically analyzed and compared between groups using One-way ANOVA test and Schffe post-hoc test at the 95% level of confidence. The result shows that chemical polymerizing automixing resin cement represents the relatively higher physical properties and shear bond strength than self-adhesive automixing resin cements.
|
|
KEYWORD
|
|
automixing resin cements, self-adhesive automixing resin cement, compressive strength, diametral tensile strength, flexural strength, shear bond strength
|
|
FullTexts / Linksout information
|
|
|
|
Listed journal information
|
|
|
|