The Journal of Advanced Prosthodontics
2015 Volume.7 No. 3 p.224 ~ p.232
The effect of IDS (immediate dentin sealing) on dentin bond strength under various thermocycling periods
Lee Sung-Bok

Lee Sang-Min
Park Su-Jung
Lee Suk-Won
Lee Do-Yun
Im Byung-Jin
Ahn Su-Jin
Abstract
PURPOSE : The purpose of this study was to find out the effect of immediate dentin sealing (IDS) on bond strength of ceramic restoration under various thermocycling periods with DBA (dentin bonding agent system).

MATERIALS AND METHODS : Fifty freshly extracted human mandibular third molars were divided into 5 groups (1 control and 4 experimental groups) of 10 teeth. We removed enamel layer of sound teeth and embedded them which will proceed to be IDS, using All Bond II. A thermocycling was applied to experimental groups for 1, 2, 7, 14 days respectively and was not applied to control group. IPS Empress II for ceramic was acid-etched with ceramic etchant (9.5% HF) and silane was applied. Each ceramic disc was bonded to specimens with Duo-link, dual curable resin cement by means of light curing for 100 seconds. After the cementation procedures, shear bond strength measurement and SEM analysis of the fractured surface were done. The data were analyzed with a one-way ANOVA and Tukey multiple comparison test (¥á=.05).

RESULTS : There were no statistically significant differences between 4 experimental groups and control group, however the mean value started to decrease in group 7d, and group 14d showed the lowest mean bond strength in all groups. Also, group 7d and 14d showed distinct exposed dentin and collapsed hybrid layer was observed in SEM analysis.

CONCLUSION : In the present study, it can be concluded that ceramic restorations like a laminate veneer restoration should be bonded using resin cement within one week after IDS procedure.
KEYWORD
Immediate dentin sealing, SEM analysis, Dentin bonding, Thermocycling, Ceramic restoration